Mild Steel Welding Wire H08mnmoa (EA2)

• Customization: Available
• Type: Rolling Wire
• Material: Copper / Copper Alloy
• Model NO.: H08MnMoA(EA2)
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 10-20mm
• Spool Size: D100mm D200mm D270mm D300mm K300mm
• Net Weight (Kg): 1kg\5kg\15kg\17kg\18kg\20kg
• C Composition(%): 0.06~0.15
• Mn Composition(%): 1.40~1.85
• Si Composition(%): 0.80~1.15
• P Composition(%): ≤0.025
• S Composition(%): ≤0.035
• Cu Composition(%): ≤0.50
• Yield Strength (MPa): ≥420
• Tensile Strength (MPa): ≥500
• Transport Package: 72spool /Pallet, 22pallets/20FT Container
• Specification: CE, ISO9001, ABS, LR, CCS, DB, TUV.
• Trademark: Marink Or OEM
• Origin: Qingdao, China
• HS Code: 7229200000
• Production Capacity: 4000 Metric Tons Per Month

Product Description

Application:
For welding hot rolled and normalization steel, such as 15MnVN, 15MnVNR, 15MnTiRe Suitable for pipe-line steel welding such as X60, X65 etc.

Conform with:
GB/T : H08MnMoA DIN : S2Mo
AWS : EA2 JIS : YS-M3

 

Wire Type	Size	inner diameter	outer diameter	Net Weight
Coil Packaging	φ1.6~5.0(mm)	300mm 620mm	400mm 820mm	25kg 250kg
TIG Wire		1 meter		5kg

 

chemical composition of welding wire(%)	C	Mn	Si	P	S	Cr	Ni	Mo	Ti	Cu
	≤0.10	1.20~1.60	≤0.25	≤0.030	≤0.030	≤0.20	≤0.30	0.30~0.50	0.15	≤0.20

 

Mechanical Properties or Deposited Metal	Yield strengthσ0.2(Mpa)	Tensile strengthσb(Mpa)	Elongationδ5(%)	AKV impact(J)
	≥440	≥540	≥17	≥27(-20)

 

Paul welding gas					SAW
Wire Size	φ0.8	φ1.0	φ1.2	φ1.6	φ2.0	φ3.0	φ4.0	φ5.0
Please be noted						Welding position
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust. Before welding please clean out the oil,rust,water etc from the work parts