Mild Steel Wire for Submerged Arc Welding H08A (EL12)

• Customization: Available
• Type: Rolling Wire
• Material: Copper / Copper Alloy
• Model NO.: H08A(EL12)
• Flux Containing: Not Containing Flux
• Spool Size: D100mm D200mm D270mm D300mm K300mm
• Net Weight (Kg): 1kg\5kg\15kg\17kg\18kg\20kg
• C Composition(%): 0.06~0.15
• Mn Composition(%): 1.40~1.85
• Si Composition(%): 0.80~1.15
• P Composition(%): ≤0.025
• S Composition(%): ≤0.035
• Cu Composition(%): ≤0.50
• Yield Strength (MPa): ≥420
• Tensile Strength (MPa): ≥500
• Transport Package: 72spool /Pallet, 22pallets/20FT Container
• Specification: CE, ISO9001, ABS, LR, CCS, DB, TUV.
• Trademark: Marink Or OEM
• Origin: Qingdao, China
• HS Code: 7229200000
• Production Capacity: 4000 Metric Tons Per Month

Product Description

Description:
EL12 (H08A)is a kind of mild steel wire for submerged arc welding. Welding together with suitable flux, the welding seam can get excellent mechanical properties.
Application:
With suitable welding flux, used to weld mild alloy steel like 09Mn2, 16Mn, 16MnCu etc submerged arc welding.
Conform with:
GB/T: H08A DIN: S1 AWS: EL12 BS: S1

 

Wire Type	Size	inner diameter	outer diameter	Net Weight
Coil Packaging	φ1.6~5.0(mm)	300mm 620mm	400mm 820mm	25kg 250kg
TIG Wire		1 meter		5kg

 

chemical composition of welding wire(%)	C	Mn	Si	P	S	Cr	Ni	Cu
	≤0.10	0.30~0.55	≤0.03	≤0.030	≤0.030	≤0.20	≤0.30	≤0.20

 

Mechanical Properties or Deposited Metal	Yield strengthσ0.2(Mpa)	Tensile strengthσb(Mpa)	Elongationδ5(%)	AKV impact(J)
	≥320	410~550	≥22	≥34(-20)

 

Wire Size(mm)			Welding position	Eletricity Polarity
φ2.0	φ2.5	φ3.0		DC+ or AC